为了制备平整的氧传感器芯片空气孔道,采用了丝网印刷的方法。相应配制了一种适印性的炭浆,优化的条件为:优选了活性炭和松油醇、最佳的球磨级配为mΦ6.5∶mΦ3=1∶2、球磨时间为12 h、分散剂含量为30%、胶含量为5%。在优化的条件下制备的空气孔道平整稳定,该制备方法具有精度高、形状平整可控、成本低以及操作简便等优点。
Abstract：In order to prepare the flat air pore canal of the lambda sensor chip, the method of screenprinting was used. A suitable carbon slurry was prepared, and the optimum conditions were as follows:activated carbon and terpineol were chosen, the grading was mΦ6.5∶mΦ3=1∶2, ball milling time was 12 h,dispersant content was 30%, rubber content was 5%. Under the optimal conditions, the smooth and sta-ble air duct was prepared. The method has the advantages of high precision, controllable shape, low costand simple operation.
[1]寇玉娟,赵莹.国Ⅳ标准实施后汽车氧传感器发展浅析[J].电子科学技术,2015,2(2):233-236.
[2]韩庆,胡劲,蒋丹宇.汽车氧传感器用电极材料的研究[J].稀有金属材料与工程,2013,42(8):1746-1750.
[3]路顺,林健,张舜.ZrO2氧传感器多孔保护层研究[J].玻璃与搪瓷,2006,34(5):7-10.
[4]徐汝玲.汽车氧传感器类型的区别[J].电子世界,2017(15):167.
[5]任继文.平板式ZrO2汽车氧传感器发展综述[J].华东交通大学学报,2007,24(4):125-130,151.
[6]王峥.平板式汽车氧传感器加热体的研制[D].北京:中国科学院大学,2013.
[7]冯冰.浅析汽车氧传感器[J].汽车维修,2013(5):14-16.
[8]周欣燕,向蓝翔,张振涛,等.车用氧传感器多孔保护层的制备及性能研究[J].材料开发与应用,2009,24(3):27-30.
[9]JURGEN R K.Automotive electronics handbook[M].2nd ed.New York:Mc Graw-Hill,1999.
[10]RIEGEL J,NEUMANN H,WIEDENMANN H M.Exhaust gas sensors for automotive emission control[J].Solid State Ionics,2002,152/153:783-800.
[11]成佐明.新型平板式浓差型汽车氧传感器结构设计及工艺的研究[D].南昌:华东交通大学,2014.
[12]张飞进,朱晓云.电子浆料用有机载体的研究现状及发展趋势[J].材料导报A:综述篇,2013,27(2):81-85.
[13]徐磊,张宏亮,刘显杰.电子浆料研究进展[J].船电技术,2012,32(S1):141-143.
[14]贺平,赵燕熹,何宝林.薄膜开关用导电碳浆的研究[J].电子元件与材料,2003,22(8):35-37.
[15]李金焕,陆建辉,王玉丰,等.碳浆油墨的制备及少量石墨烯对碳浆油墨性能的影响[J].科学技术与工程,2015,15(14):92-96.
[16]何泽刚,申荣卫,韩炯刚.汽车用氧化锆式氧传感器应用现状与发展趋势[J].传感器世界,2014,20(3):7-11.
[17]姜礼义,周晓,陈千伟.宽域氧传感器性能检测系统的研制[J].中国科技纵横,2017(19):84,86.
基本信息:
DOI：10.16389/j.cnki.cn42-1737/n.2018.03.006
中图分类号:TP212;TS871.1
引用信息:
[1]宋斌,曹文杰,尤庆亮.基于炭浆的氧传感器空气孔道制备[J].江汉大学学报(自然科学版),2018,46(03):231-237.DOI:10.16389/j.cnki.cn42-1737/n.2018.03.006.
基金信息: